aluminum powder product

Is generally used H&X white fused alumina supplier, kaolin, clay or other material containing Al2O3 in an amount of carbon added, then heated to 1300 ~ 1500 ℃ in a nitrogen atmosphere, the product was obtained Si3N4. Which nitrogen used must ensure that no oxygen. Silica fume on the direct nitridation nitrogen, ammonia or hydrogen nitrogen gas mixture heated to 1200 ~ 1450 ℃ direct nitriding system. The reaction can be prepared with a high content of α original H&X Sic Refractory powder 1200 ~ 1300 ℃, high strength sintered ceramic. Reduction of silica to silicon dioxide, silicon nitride, nitrogen and carbon as the raw material preparation, the following reaction formula. The silica (or TEOS hydrolysis of silica) mixed with a certain proportion of carbon, nitrogen gas was heated to 1400 ℃ nitride 24h.